Type 201 stainless steel is a low nickel, high-work hardening, austenitic chromium-nickel-manganese stainless steel. Type 201 stainless steel is not hardenable by heat treatment. It may be substituted, in some cases, for other higher nickel content alloys.
Chemical Composition of 201 Stainless Steel Cold Rolled Steel
| Grade | C | Mn | Si | P | S | Cr | Ni | N |
| SS 201 | 0.15 max | 5.5 – 7.5 | 100 max | 0.06 max | 0.03 max | 16.00-18.00 | 0.3 – 0.5 | – |
Mechanical Properties of Grade 201 Stainless Steel Cold Rolled Steel
| Properties | Metric | Imperial |
| Tensile strength (transverse at room temperature) | 685 MPa | 99400 psi |
| Tensile strength (longitudinal at room temperature) | 696 MPa | 101000 psi |
| Yield strength (transverse at room temperature) | 292 MPa | 42400 psi |
| Yield strength (longitudinal at room temperature) | 201 MPa | 43700 psi |
| Compressive yield strength | 365 MPa | 52900 psi |
| Elastic modulus | 197 GPa | 28573 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (longitudinal at room temperature) | 56% | 56% |
| Elongation at break (transverse at room temperature) | 62.50% | 62.50% |
| Hardness, Rockwell B (transverse at room temperature) | 85 | 85 |
| Hardness, Rockwell B (longitudinal at room temperature) | 85 | 85 |
The majority of normal processing can be performed on 201 Stainless Steel sheet Jainex Steel & Metal Offers Following Processing for 201 Stainless Steel sheet:
201 Stainless Steel sheet Testing
201 Stainless Steel sheet Cutting
201 Stainless Steel sheet Grinding
201 Stainless Steel sheet Forming Drilling/ Machining